Quick Details

  • Standard: AISI, ASTM
  • Dimensions: 0
  • Place of Origin: Maharashtra, India
  • Brand Name: BHARAT AEROSPACE
  • Type: Round
  • Application: Pump Shaft
  • Shape: Round
  • Certification: ISO
  • Special Use: Valve Steels
  • OTHER STANDARD: UNS S41600, ASTM A582

Packaging & Delivery

Packaging Details 1) Export Worthy Packaging
2) As Per Buyers Requirement
Delivery Time Delivery On Time

Specifications

STAINLESS STEEL 416 ROUND BARS
1) High quality.
2) Reasonable price.
3) Delivery on time.
4) Quality Assurance.

Availability

Stainless Steel 416 is stocked by 110 North American distributors and produced by 41 large mills. Distributors will offer small quantity buys while mills will generally only sell large quantities, with delivery times anywhere from 10 to 50 weeks depending on size and form required

This material is stocked primarily in Bar Products by 99 distributors but is also available to a lesser extent in Wire Products, Flat Rolled Products, Fasteners, Tubular Products, Casting Products, Forging Products, Piping Components, and Shapes.

 


Specifications

The following specifications cover Stainless Steel 416

 

  • AISI 416
  • AMS 5610
  • ASTM A194 (416, 6F)
  • ASTM A314
  • ASTM A473
  • ASTM A581
  • ASTM A582
  • ASTM A895
  • DIN 1.4005
  • UNS S41600
 
 
 
 
 
 

 


Chemistry Data : [top]

 

Carbon

 

0.15 max

Chromium

 

12 - 14

Iron

 

Balance

Manganese

 

1.25 max

Molybdenum

 

0.6 max

Phosphorus

 

0.06 max

Silicon

 

1 max

Sulphur

 

0.15 min


Principal Design Features 416 was the first free machining stainless steel. It is a heat treatable chromium steel with excellent machinability and non-galling characteristics. The alloy is magnetic in all conditions.

Applications A wide variety of screw machine parts including nuts, bolts, screws, gears and pinions, valve trim, shafts and axles.

Machinability Speeds and feed comparable with those of some of the free machining carbon steels. Good chip breakage. Material heat treated at 200 F and cold drawn will give best results.

Welding Welding of any type is not recommended, as the high sulfur content creates porosity.

Hot Working All hot work procedures should commence following uniform heating to 2100-2250 F (1149-1232 C). Hot work below 1700 F (927 C) may result in cracking.

Cold Working This alloy will accept only minor cold working. Severe deformation will result in cracking.

Annealing 1200-1400 F (650-760 C), air cool. For maximum softness, 1500-1650 F (816-900 C), furnace cool.

Tempering Temper to achieve properties desired. Avoid tempering in the range of 750-1050 F (399-566 C) to avoid a decrease in impact strength and corrosion resistance.

Hardening Soak at 1700-1850 F (927-1010 C) oil quench.

Transaction History of the Supplier

Below is the information about the supplier's transactions conducted via Alibaba.com. If you require further details regarding the transaction data, please contact the supplier directly.

Transaction Overview

Transactions

Transaction Details

This supplier has completedtransactions with buyers from .

Shipping Destination
Transaction Value
Transaction Date
Email to this supplier
The supplier supports Trade Assurance – A free service that protects your orders from payment to delivery.
Supplier's Trade Assurance Limit: US $
Learn More